1475 Werkstoff Deutschland Europa Frankreich Großbritannien Italien Schweden Spanien USA Nr.: Germany Europe France Great Britain Italy Sweden Spain USA material DIN EN AFNOR BS UNI SIS UNE AISI No.: Werkstoffgruppe / material group 7. Gusseisen / Cast iron Werkstoffgruppe / material group 8. Gehärtete Stähle / Hardened materials Werkstoffgruppe / material group 9. Alulegierungen / Aluminum alloys 7.1 Grauguss bis 180 HB / grey cast iron up to 180 HB / GG 0.6010 GG10 GJL-100 Ft 10 B G 10 0110-00 FG 10 A48-20 B 0.6012 GG150HB GJL-HB 170 0.6015 GG15 GJL-150 Ft 15 D Grade 150 G 15 0115-00 FG 15 A48-25 B 0.6017 GG170HB GJL-HB 205 7.2 Grauguss bis 350 HB / grey cast iron up to 350 HB / GG 0.6020 GG20 GJL-200 Ft 20 D Grade 220 G 20 0120-00 FG 20 A48-30 B 0.6022 GG190HB GJL-HB 230 0.6025 GG25 GJL-250 Ft 25 D Grade 260 G 25 0125-00 FG 25 A48-40 B 0.6027 GG220HB GJL-HB 250 0.6030 GG30 GJL-300 Ft 30 D Grade 300 G 30 0130-00 FG 30 A48-45 B 0.6032 GG240HB GJL-HB 275 0.6035 GG35 GJL-350 Ft 35 D Grade 350 G 35 0135-00 FG 35 A48-50 B 0.6037 GG260HB GJL-HB_275 0.6040 GG40 GJL-400 Ft 40 D Grade 400 0140-00 A48-60 B 7.3 Kugelgraphitguss bis 200 HB / modular cast iron up to 200 HB / GGG 0.6652 GGLNiMn137 GJLA-XNiMn 13-7 L-NM 13 7 L-NiMn 13 7 0.6655 GGLNiCuCr1562 GJLA-XNiCuCr 15-6-2 L-NUC 15 6 2 L-NiCuCr 15 6 2 A 436 Type 1 0.6656 GGLNiCuCr1563 GJLA-XNiCuCr 15-6-3 L-NUC 15 6 3 L-NiCuCr 15 6 3 A 436 Type 1b 0.6660 GGLNiCr202 GJLA-XNiCr 20-2 L-NC 20 2 L-NiCr 20 2 0523-00 A 436 Type 2 0.7033 GGG353 0.7040 GGG40 FGS 400-12 420/12 GS 400-12 0717-02 60-40-18 0.7043 GGG403 FGS 370-17 370/17 GSO 42/15 0717-15 0.7050 GGG50 FGS 500-7 500/7 GS 500/7 0727-02 65-45-12 0.7652 GGGNiMn137 GJSA-XNiMn S-Mn 13 7 S-NiMn 13 7 0772-00 0.7659 GGGNiCrNb202 GJSA-XNiCrNb 20-2 0.7660 GGGNiCr202 GJSA-XNiCr 20-2 L-NC 20 2 L-NiCuCr 20 2 0523-00 A 439 Type D-2 0.7665 GGGNiSiCr2052 GJSA-XNiSiCr 20-5-2 S-NSC 20 5 2 S-NiSiCr 20 5 2 0.7670 GGGNi22 GJSA-XNi 22 S-N 22 S-Ni 22 A 439 Type D-2C 07673 GGGNiMn234 GJSA-XNiMn 23-4 S-NiMn 23 4 A 571 Type D-2M GGGV30 GGGV30 7.4 Kugelgraphitguss bis 250 HB / modular cast iron up to 250 HB 0.6661 GGLNiCr203 GJLA-XNiCr 20-3 L-NiCr 20 3 A 436 Type 2b 0.6667 GGLNiSiCr2053 GJLA-XNiSiCr 20-5-3 L-NSC 20 5 3 L-NiSiCr 20 5 3 0.7060 GGG60 FGS 600-3 600/3 GS 200/3 0732-03 80-55-06 0.7070 GGG70 FGS 700-2 700/2 GS 700-2 0737-01 100-70-03 7.5 Temperguss 130 HB / malleable cast iron up to 130 HB 0.8038 GTWS3812 GJMW-360-12 0.8040 GTW4005 GJMW-400-5 MB 40-10 GMB 40 0.8045 GTW4507 GJMW-450-7 GMB 45 0.8055 GTW55 GMB 55 0.8065 GTW65 GMB 65 0.8135 GTS3510 GJMB-350-10 MN 35-10 B 340/12 0815 32510 0.8145 GTS4506 GJMB-450-6 P 440/7 0852 40010 7.6 Temperguss 230 HB / malleable cast iron up tp 230 HB 0.8035 GTW3504 GJMW-350-4 0.8155 GTS5504 GJMB-550-4 MP 50-5 P 510/4 0854 50005 0.8165 GTS6502 GJMB-650-2 MP 60-3 P 570/3 0858 70003 0.8170 GTS7002 GJMB-700-2 Mn 700-2 P 690/2 GMN 70 0862 90001 8.1 Toolox 44 45-55 HRC 45-55 HRC 45-55 HRC 45-55 HRC 45-55 HRC 45-55 HRC 45-55 HRC 45-55 HRC 8.11 Toolox 33 850-1100 N/mm2 850-1100 N/mm2 850-1100 N/mm2 850-1100 N/mm2 850-1100 N/mm2 850-1100 N/mm2 850-1100 N/mm2 850-1100 N/mm2 8.2 Gehärtet 55-60 HRC 55-60 HRC 55-60 HRC 55-60 HRC 55-60 HRC 55-60 HRC 55-60 HRC 55-60 HRC 8.3 Gehärtet 60-70 HRC 60-70 HRC 60-70 HRC 60-70 HRC 60-70 HRC 60-70 HRC 60-70 HRC 60-70 HRC 8.4 Hartguss bis 48 HRC / hardened cast iron up to 48 HRC 0.9620 GX260NiCr42 GJH-X260NiCr 4-2 Grade 2 A 0512-00 A532 I B NiCr-LC 0.9625 GX330NiCr42 GJH-X330NiCr 4-2 Grade 2 B 0513-00 A532 I A NiCr-HC 0.9630 GX300CrNiSi952 GJH-X300CrNiSi 9-5-2 Grade 2 C A532 I D Ni-HiCr 0.9635 GX300CrMo153 GJH-X300CrMo 15-3 Grade 3 A A532 IIC15% CrMo-HC 9.1 Alu-Knetlegierungen bis 250 N/mm2 / malleable alu alloy up to 250 N/mm2 3.0255 Al99.5 A 59050 C L 31 1000 3.0280 Al99.8 3.0515 GAl995 3.3292 GDAlMg9 3.3315 AlMg1 AW-6082 3.3535 AlMg3 3.3547 AlMg4,5Mn 3.3555 AlMg5 9.2 Alu-Knetlegierungen bis 350 N/mm2 / malleable alu alloy up to 350 N/mm2 3.0615 AlMgSiPb 3.1325 AlCuMg1 AW-2017 A 3.1355 AlCuMg2 AW-2024 Internationaler Normenvergleich International comparison of standards K N H 10 Index 9 8 OIL 7 MACHINES 6 5 4 3 2 1
RkJQdWJsaXNoZXIy MTgxNTQ=